Products Process Explanation Advantages
EPS-1000 Electrolytic polishing
  • EPS-1000 is a electrolytic polishing agent for stainless steel with additives mixed in sulfuric acid bath, which is used for obtaining a beautiful high bright in most of stainless-steel materials. One solution process for both make-up and replenish makes it possible to easy control
  • Possible to obtain uniform and level surface as good as in the phosphoric/sulfuric bath
  • Economical in mass processing due to time reduction as it can be reduce the buffing operation
  • Preferentially polishing the surface protrusions for reducing surface friction more than mechanical polishing
  • As it can improve the appearance of the material, the compressive stress and ductility that occur during metal processing can be suppressed or reduced
EPS-2000 Electrolytic polishing
  • EPS-2000 is a electrolytic polishing agent for stainless steel with additives mixed in phosphoric acid/sulfuric acid bath, which is used for obtaining a beautiful high gloss in most of stainless-steel materials. One solution process for both make-up and replenish makes it possible to easy control
  • Possible to obtain more uniform surface and better leveling than in the phosphoric/sulfuric bath
  • Economical in mass processing due to time reduction as it can be reduce the buffing operation
  • Preferentially polishing the surface protrusions for reducing surface friction more than mechanical polishing
  • As it can improve the appearance of the material, the compressive stress and ductility that occur during metal processing can be suppressed or reduced
EPS-850 Electrolytic polishing
  • EPS-850 is a sulfuric-acid-bath-type electrolytic polishing agent for stainless steel, which is used for obtaining a beautiful high bright in most of stainless-steel materials
  • Brings excellent polishing effect on most materials
  • Brings excellent bright effect even on carbon steel with rough surface
  • Economical because of time saving as it can reduce buffing work in mass processing
  • Preferential polishing of surface protrusions helps to decrease the surface friction compared to mechanical polishing.
  • As it can improve the appearance of the material, the compressive stress and ductility that occur during metal processing can be suppressed or reduced
EPS-950 Electrolytic Polish applied
  • EPS-950 is an additive-type electrolytic polishing agent applied in phosphoric/sulfuric acid bath, with which we can obtain beautiful high bright in most stainless-steel materials
  • Prevents surface discoloration due to heat treatment and/or oxidation and provides an anti-corrosion surface
  • Additive improves surface reflectance and brightness compared to when using only phosphoric/sulfuric acids
  • Flattens the fine peaks and valleys of the surface to improve roughness
  • Removes iron and increases chromium/nickel content in the surface while passivating the stainless steel and reducing surface friction
  • Possible to improve the appearance of the material and restrain or reduce the compressive stress and ductility during metal forming process
SP-250 Passivation
  • SP-250 is a passivating agent for stainless steels, which suppresses corrosion of the materials by passivating most of them
  • Enhances corrosion resistance of stainless steel
  • Provides uniform and smooth appearance and finish
  • Safe and eco-friendly because it does not contain nitric acid
  • Removes only iron without removing any other elements from the target material
  • Does not allow any heavy metal (hazardous waste) to flow into the bath
SR-200 Welding Scale Remover
  • SR-200 is a Welding scale remover of stainless steel caused by welding
  • As the scale is removed, it is cleaned thoroughly at the same time
  • Contains no chromic acid
  • Pickling and passivation are carried out at the same time
  • No gas generation
  • The coating film is easily removed by rubbing or washing with water
SE-100 Etching
  • SE-100 is an etchant that can remove foreign substances and scales stuck on stainless steel materials
  • Contaminated substances stuck on SUS material can be removed
  • Depending on the concentration, there is no over corrosion of the material
  • Improved surface roughness
  • Uniform etching and precise etching are possible, resulting in excellent adhesion during the posttreatment process
  • The generation of Nox gas harmful to the human body is minimal, so it is effective in improving the working environment